STATPAK™ HB 3600
Opaque Anti Static Moisture Barrier EMI
Meets the requirements for MIL-PRF-81705D
This material offers excellent moisture barrier
properties with a moisture vapour transmission rate of < 0.02
gms/24 hours. Full protection against ESD, EMI, RFI and
tribo charging is also given. This material is designed for
vacuum packaging.
Construction/Composition
(from outermost to innermost layer)
Static dissipative layer/aluminised special polyester
film/adhesive/2.6mil polyolefin Heat-seal/static dissipative
layer. Contains no amines or n-octanoic acid, polycarbonate
compatible.
Standard Sizes
| Inch |
MM |
| 4x26 |
100x650 |
| 6x28 |
150x700 |
| 10x30 |
250x750 |
| 16x18 |
400x450 |
| 18x18 |
450x450 |
Moisture Barrier Bags are available to order in
any size from 3" X 3" to 48" X
88" and from 75 X 75mm to 1200X 2000mm.
Print Options
Bags can be custom printed using hot foil stamps
or flexo printing. Bags are available with open tops, zip close
tops, or self adhesive/ tamper evident closures.
Technical Specifications
Physical Properties
|
Yield (per pound)
|
7100 square inches
|
|
Total Thickness
|
3.6mils(92 microns)
|
|
Tensile Strength (ASTM
D88-83 Method A)
|
MD:9,000psi TD:10,500 psi
|
|
Tear Strength (ASTM
D1004-66Notched)
|
MD: 4.7lbs TD 4.3 lb
|
|
Elongation (ASTM D882-83
Method A)
|
MD:98% TD:80%
|
|
Burst Strength (FTMS 101-C
Method 2007 la)
|
84 psi
|
|
Puncture Strength (FTMS
101-C Method 2065.1)
|
>20 psi
|
|
Heat Seal Strength (ASTM D
1876-72)Vertrod Sealer
|
>11 lb /in width
|
|
Light transmission (ASTM
D1003-77)
|
<.01%
|
|
MVTR (ASTM F-1249 @ 100F
100sq in/24hrs)
|
<.02gms .01gms nominal
|
|
Seam Strength (Mil B81705
REV-C) before & after ageing
|
160°F = No separation 100°F = No
Separation, Room Temp = No Separation
|
|
Delamination (FTMS 101-c
Method 3015)
|
No leakage, swelling,
embrittlement
|
|
Water Resistance (FTMS
101-C Method 3028 procedure F)
|
No delamination
|
|
Resistance to Ageing (MIL-PRF-81705D )
|
No delamination
|
|
OTR (ASTM D3985 100% Oxygen
100 sq.in/24 hrs) 77°F, 0%:90% R.H.
|
0.0005 cc <0.005 cc
|
Electrical Properties
|
EMI Shielding (Mil
81705-Rev-C)
|
> 40 dB Between 1 & 10Ghz
|
|
Resistivity - Conductive Metal layer
(ASTM D-257)
|
< 2 Ohms/sq. in
|
|
Capacitative Probe Test (High
Voltage Discharge)-EIA -Std 541/Appendix E - 1KV)
|
< 8Volts
|
|
Static Decay (FTMS 101C,
Method 4046. 1, 5000 to 0 Volts)
|
< 0.05 seconds
|
|
Surface Resistivity (both surfaces)
-(ASTM D-257 @12%RH)
|
< 1012 Ohms/sq in avg
1010 Ohms/sq in
|
|
Charge Generation -nominal (Modified
incline plane avg. nC/sq.in):
|
Teflon -0.09
Quartz +0.1
|
Contact Corrosivity
-
Low Carbon Steel, Aluminium , Copper, AG
plated copper foil, Sn-Pb coated copper foil, Stainless Steel,
Kovar
-
No evidence of Corrosion, Pitting or Etching
of Metal
The values shown above were developed from random samples taken from production material.
We believe them to be typical for this particular product. Because of normal lot to lot
variations,actual values may vary somewhat from these depicted here. Faulkner Export
Packaging Ltd makes no warranty, express or implied, as to the suitability of these
materials for any specific purpose. Consumers should determine suitability through
their own testing and evaluation.
|
|